Stainless Steel Plate

Short Description:

Pipe type:Stainless Steel Plate,stainless steel sheet,metal sheet,Stainless steel Plate,Steel Plate,Cold rolled steel plate ,Hot Rolled Stainless Steel Plate,Stainless Steel Sheet Plate,304 Stainless Steel Plate, 316 Stainless Steel Plate

Thickness :0.01~200mm

Width:1000mm,1219mm,1500mm,1800mm,2000mm,2500mm,3000mm,3500mm,etc

Length :2000mm,2440mm,3000mm,5800mm,6000mm,etc

Material:310S,310,309,309S,316,316L,316Ti,317,317L,321,321H,347,347H,304,304L,302,301,201,202,403,405,409,409L,410,410S,420,430,631,904L,Duplex,etc

Surface:Common:2B, 2D, HL(Hailine), BA(Bright annealed), No.4.

Packing:Waterproof Paper Wrapped, Packed in Wooden Cabins

Send email to us

Product Detail

Product Tags

Introduction

Thickness :0.01~200mm

Width:1000mm,1219mm,1500mm,1800mm,2000mm,2500mm,3000mm,3500mm,etc

Length :2000mm,2440mm,3000mm,5800mm,6000mm,etc

Material:310S,310,309,309S,316,316L,316Ti,317,317L,321,321H,347,347H,304,304L,302,301,201,202,403,405,409,409L,410,410S,420,430,631,904L,Duplex,etc

Surface:Common:2B, 2D, HL(Hailine), BA(Bright annealed), No.4.

Packing:Waterproof Paper Wrapped, Packed in Wooden Cabins

Specification

Chemical Properties of Frequently-used Stainless Steel Material Grade
UNS	ASTM	EN	JIS	C%	Mn%	P%	S%	Si%	Cr%	Ni%	Mo%
S20100	201	1.4372	SUS201	≤0.15	5.5-7.5	≤0.06	≤0.03	≤1.00	16.0-18.0	3.5-5.5	-
S20200	202	1.4373	SUS202	≤0.15	7.5-10.0	≤0.06	≤0.03	≤1.00	17.0-19.0	4.0-6.0	-
S30100	301	1.4319	SUS301	≤0.15	≤2.00	≤0.045	≤0.03	≤1.00	16.0-18.0	6.0-8.0	-
S30400	304	1.4301	SUS304	≤0.08	≤2.00	≤0.045	≤0.03	≤0.75	18.0-20.0	8.0-10.5	-
S30403	304L	1.4306	SUS304L	≤0.03	≤2.00	≤0.045	≤0.03	≤0.75	18.0-20.0	8.0-12.0	-
S30908	309S	1.4833	SUS309S	≤0.08	≤2.00	≤0.045	≤0.03	≤0.75	22.0-24.0	12.0-15.0	-
S31008	310S	1.4845	SUS310S	≤0.08	≤2.00	≤0.045	≤0.03	≤1.50	24.0-26.0	19.0-22.0	-
S31600	316	1.4401	SUS316	≤0.08	≤2.00	≤0.045	≤0.03	≤0.75	16.0-18.0	10.0-14.0	2.0-3.0
S31603	316L	1.4404	SUS316L	≤0.03	≤2.00	≤0.045	≤0.03	≤0.75	16.0-18.0	10.0-14.0	2.0-3.0
S31703	317L	1.4438	SUS317L	≤0.03	≤2.00	≤0.045	≤0.03	≤0.75	18.0-20.0	11.0-15.0	3.0-4.0
S32100	321	1.4541	SUS321	≤0.08	≤2.00	≤0.045	≤0.03	≤0.75	17.0-19.0	9.0-12.0	-
S34700	347	1.4550	SUS347	≤0.08	≤2.00	≤0.045	≤0.03	≤0.75	17.0-19.0	9.0-13.0	-
S40500	405	1.4002	SUS405	≤0.08	≤1.00	≤0.04	≤0.03	≤1.00	11.5-14.5	≤0.60	-
S40900	409	1.4512	SUS409	≤0.08	≤1.00	≤0.045	≤0.03	≤1.00	10.5-11.75	≤0.50	-
S43000	430	1.4016	SUS430	≤0.12	≤1.00	≤0.040	≤0.03	≤0.75	16.0-18.0	≤0.60	-
S43400	434	1.4113	SUS434	≤0.12	≤1.00	≤0.040	≤0.03	≤1.00	16.0-18.0	-	-
S44400	444	1.4521	SUS444L	≤0.025	≤1.00	≤0.045	≤0.03	≤1.00	17.5-19.5	≤1.00	-
S40300	403	-	SUS403	≤0.15	5.5-7.5	≤0.04	≤0.03	≤0.50	11.5-13.0	≤0.60	-
S410000	410	1.40006	SUS410	≤0.15	≤1.00	≤0.035	≤0.03	≤1.00	11.5-13.5	≤0.60	≤1.00
S42000	420	1.4021	SUS420J1	0.16~0.25	≤1.00	≤0.04	≤0.03	≤1.00	12.0-14.0	≤0.75	≤1.00
S440A	440A	1.4028	SUS440A	0.60~0.75	≤1.00	≤0.04	≤0.03	≤1.00	16.0-18.0	-	≤0.75
S32750	SAD2507	1.4410		≤0.03	≤1.2	≤0.035	≤0.02	≤0.80	24.0-26.0	6.0-8.0	3.0-5.0
S31803	SAF2205	1.4462		≤0.03	≤2.0	≤0.03	≤0.02	≤1.00	21.0-23.0	4.0-6.5	2.5-3.5
N08904	904L	1.4539		≤0.0.3	≤2.0	≤0.035	≤0.03	≤1.00	18.0-20.0	23.0-25.0	3.0-4.0

310/ 310S stainless steel sheet

310 stainless steel austenitic chromium nickel stainless steel has good oxidation resistance, corrosion resistance, because the higher percentage of chromium and nickel, 310 has much better creep strength, can continuously work under high temperature, good heat resistance.

310S stainless steel is austenitic chromium nickel stainless steel, has a good 310S stainless steel oxidation resistance, resistance Corrosive.

The differences of chemical composition for 310/310S stainelss steel

Grade	C(%)	Si(%)	Mn(%）	P（%）	S(%）	Cr(%)	Ni(%)	N(%)	Cu(%)
310	≤0.25	≤1.0	≤2.0	≤0.03	---	24.0-26.0	19.0-22.0	---	---
310S	≤0.08	≤1.0	≤2.0	≤0.03	≤0.03	24.0-26.0	19.0-22.0	---	---

The differences of Mechanical property for 310/310S stainless steel

Grade	tensile strengthMpa	Yield StrengthMpa	Elongation(%)	rate of reduction in area(%)	Density(g/cm3)
310	≥470	≥17	≥40	≥50	7.98
310S	≥520	≥205	≥40	≥50	7.98

304/ 304L/ 304H stainless sheet

About 304 material:304 stainless steel is a common stainless steel material, the density of 7.93 g/cm3, the industry is also called 18/8 stainless steel. High temperature resistance of 800 degrees, with good processing performance, high toughness characteristics, widely used in industrial and furniture decoration industry and food industry.

About 304L material:304L steel as a low C in the general state, its corrosion resistance and 304 similar, but after welding or stress after its excellent corrosion resistance to the grain boundary. In the case without heat treatment, can remain good corrosion resistance, generally use 400 or less (non-magnetic, temperature -196 degrees Celsius to 800 degrees Celsius). Widely used to produce good overall performance requirements (corrosion resistance and formability) of equipment and parts.

About 304H material: 304H is a kind of stainless steel, with good bending, welding process performance, corrosion resistance, high durability and organizational stability, cold deformation ability is very good. The highest temperature can reach 650 DEG C, and the oxidation resistance is up to 850 DEG C

The differences of Chemical composition for 304 304L 304H

Grade	C(%)	Si(%)	Mn(%)	P(%)	S(%)	Cr(%)		Ni(%)	N(%)
304	≤0.08	≤0.75	≤2.0	≤0.045	≤0.03	18.0-20.0		8.0-10.5	≤0.1
304L	≤0.03	≤0.75	≤2.0	≤0.045	≤0.03	18.0-20.0	8.0-12.0		≤0.1
304H	0.04-1.0	≤0.75	≤2.0	≤0.045	≤0.03	18.0-20.0		8.0-10.5	----

The differences of Mechanical property for 304 304L 304H

Grade	tensile strength(Mpa)	Yield Strength(Mpa)	Elongation(%)	Hardness(HR)
304	≥515	≥205	≥40	≥92
304L	≥485	≥170	≥40	≥92
304H	≥515	≥205	≥40	≥92

316/ 316L stainless steel sheet

About 316 material:316 stainless steel by adding Mo element, the corrosion resistance, and high temperature strength has greatly improved, high temperature can reach 1200-1300 degrees, can be used in severe conditions.Corrosion resistance is better than 304 stainless steel, in pulp and paper production process has good corrosion resistance. And 316 stainless steel is also resistant to erosion of marine and corrosive industrial atmosphere.

About 316L material: 316L stainless steel has a carbon content of less than 316, which is commonly used in pulp and paper equipment heat exchangers, dyeing equipment, film washing equipment, pipelines, coastal areas outside the building materials. Corrosion resistance is better than 316 material.

The differences of chemical composition for 316 316L stainless steel

Grade	C(%)	Si(%)	Mn(%)	P(%)	S(%)	Cr(%)	Ni(%)	Mo(%)	Cu(%)
316	≤0.08	≤1.0	≤2.0	≤0.045	≤0.03	16.0-18.0	10.0-14.0	2.0-3.0
316L	≤0.03	≤1.0	≤2.0	≤0.045	≤0.03	16.0-18.0	10.0-14.0	2.0-3.0

The differences of Mechanical property for 316 316L stainless steel

Grade	tensile strengthMpa	Yield StrengthMpa	Elongation(%)	rate of reduction in area(%)	Density(g/cm3)
316	≥520	≥205	≥40	≥60	7.98
316L	≥480	≥177	≥40	≥60	7.98

430 stainless steel sheet

430 stainless steel is a good corrosion resistance of common steel, thermal performance than austenitic good, thermal expansion coefficient than austenitic small, heat fatigue, add stabilization element titanium, weld parts mechanical performance is good.

430 stainless steel used in architectural use, fuel burner parts, household appliances, home appliance parts.

Chemical composition for 430 stainelss steel